通焊接風(fēng)管是由鍍鋅和不銹鋼兩種材質(zhì)的鋼帶經(jīng)過(guò)焊接工藝成型的管道，焊接口緊密、密封性好，可過(guò)水不漏，確?？蛻羰褂貌宦┯筒宦┧娘L(fēng)管，風(fēng)管的通焊接風(fēng)管是由鍍鋅和不銹鋼兩種材質(zhì)的鋼帶經(jīng)過(guò)焊接工藝成型的管道，焊接口緊密、密封性好，可過(guò)水不漏，確?？蛻羰褂貌宦┯?不漏水的風(fēng)管，風(fēng)管的使用壽命長(zhǎng)達(dá)10年以上，適用于中高壓排風(fēng)除塵系統(tǒng)及廢氣處理系統(tǒng)，風(fēng)管可做成2.44米3米6米8米一接（建議用2.44-3米一節(jié)）。焊接風(fēng)管廣泛應(yīng)用于工廠和工業(yè)生產(chǎn)中。焊接風(fēng)管又稱焊管，是由鋼板或鋼帶壓接成型后制成的固定長(zhǎng)度為6m的鋼管，具有生產(chǎn)工藝簡(jiǎn)單、生產(chǎn)效率高、品種規(guī)格多、設(shè)備投資少等優(yōu)點(diǎn)，但其綜合強(qiáng)度低于無(wú)縫鋼管。

The through welding air duct is a pipeline formed by welding two types of steel strips, galvanized and stainless steel, with tight welding joints and good sealing, which can pass through water without leakage, ensuring that customers use air ducts without oil or water leakage. The through welding air duct of the air duct is a pipeline formed by welding two types of steel strips, galvanized and stainless steel, with tight welding joints and good sealing, which can pass through water without leakage, ensuring that customers use air ducts without oil or water leakage, The service life of the air duct can reach more than 10 years, suitable for medium and high pressure exhaust and dust removal systems and waste gas treatment systems. The air duct can be made into a 2.44-3-meter-6-8-meter-long joint (it is recommended to use a 2.44-3-meter-long joint). Welded air ducts are widely used in factories and industrial production. Welded air duct, also known as welded pipe, is a steel pipe with a fixed length of 6m made by pressing and forming steel plates or steel strips. It has the advantages of simple production process, high production efficiency, multiple varieties and specifications, and low equipment investment, but its comprehensive strength is lower than that of seamless steel pipes.

1、焊前準(zhǔn)備

1. Preparation before welding

（1）根據(jù)板厚形式，坡口加工采用機(jī)加工、等離子弧切割或碳弧氣刨。采用碳弧氣刨、坡口和手工電弧焊時(shí)，為避免飛濺金屬的損傷，應(yīng)在坡口兩側(cè)涂石灰粉。

(1) According to the thickness form of the plate, groove processing adopts machining, plasma arc cutting, or carbon arc air gouging. When using carbon arc air gouging, bevel welding, and manual arc welding, to avoid damage from splashing metal, lime powder should be applied on both sides of the bevel.

（2）應(yīng)采用V型坡口，焊接電流應(yīng)小，以防止不銹鋼的晶間腐蝕。

(2) V-shaped grooves should be used, and the welding current should be small to prevent intergranular corrosion of stainless steel.

（3）為了滿足相同性能的接頭，焊接材料的選擇應(yīng)遵循“等成分”的原則。同時(shí)應(yīng)注意風(fēng)管焊接接頭中的鐵素體含量不宜過(guò)多，以提高接頭的抗熱裂和抗晶間腐蝕的能力。

(3) In order to meet the same performance of joints, the selection of welding materials should follow the principle of "equal composition". At the same time, it should be noted that the ferrite content in the welded joints of air ducts should not be too high to improve the joint's ability to resist thermal cracking and intergranular corrosion.

（4）采用嚴(yán)格的定位焊，遵循“短而厚”和“不焊透點(diǎn)焊”的原則。

(4) Strict positioning welding is adopted, following the principles of "short and thick" and "non penetration spot welding".

2、焊接技術(shù)要求

2. Welding technical requirements

（1）手工電弧焊采用直流反接，氬弧焊采用直流電連接。

(1) Manual arc welding adopts DC reverse connection, while argon arc welding adopts DC connection.

（2）風(fēng)管焊接前，用不銹鋼絲將焊絲表面的氧化皮刷掉，用丙酮清洗干凈，然后晾干，隨時(shí)使用。

(2) Before welding the air duct, brush off the oxide layer on the surface of the welding wire with stainless steel wire, clean it with acetone, then air dry and use it at any time.

（3）打底焊時(shí)，焊縫厚度應(yīng)盡量薄，有利于與根部熔合良好；熄弧時(shí)，應(yīng)呈緩坡?tīng)睿缬兄够】s孔，應(yīng)用拋光機(jī)打磨掉。必須在坡口內(nèi)起弧和滅弧，并填滿弧坑，防止弧坑開(kāi)裂。

(3) When backing welding, the thickness of the weld seam should be as thin as possible, which is conducive to good fusion with the root; When extinguishing the arc, it should be in a gentle slope shape. If there is any arc stopping shrinkage hole, it should be polished off with a polishing machine. Arc initiation and extinguishing must be carried out within the groove, and the arc crater must be filled to prevent cracking.

（4）為防止碳化物析出敏化和晶間腐蝕，應(yīng)嚴(yán)格控制層間溫度和焊后冷卻速度，將層間溫度控制在60℃以下。

(4) To prevent carbide precipitation sensitization and intergranular corrosion, the interlayer temperature and post weld cooling rate should be strictly controlled, and the interlayer temperature should be controlled below 60 ℃.

（5）焊接時(shí)盡量采用氬弧焊手柄技術(shù)，該工藝能控制焊接層的表面顏色和形狀，焊接效果理想。

(5) When welding, try to use argon arc welding handle technology as much as possible. This process can control the surface color and shape of the welding layer, and the welding effect is ideal.